ASTM A 106 Black Carbon Seamless Steel Pipe


ASTM A 106 Black Carbon Seamless Steel Pipe
Standard: ASTM A106/A106M
This specification covers carbon steel pipe for high-temperature service.
Application of ASTM 106 Carbon Seamless Steel Pipe:
Pipe ordered under this specification shall be suitable for bending, flanging, and similar forming operations, and for welding. When the steel is to be welded, it is presupposed that a welding procedure suitable to the grade of steel and intended use or service will be utilized.
Manufacturing Process of ASTM A106 Seamless Steel Tube:
ASTM A106 seamless steel pipe are produced either by cold-drawn or hot rolled, as specified.
Hot finished pipe need not heat treated. When hot finished pipe is heat treated, it shall be heat treated at a temperature of 1200°F or higher. Cold drawn pipe shall be heat treated after final cold draw pass at a temperature of 1200°F or higher.
Details of ASTM A106 Seamless Steel Pipe We can supply:
Manufacture:Seamless process, cold drawn or hot rolled
Cold drawn: O.D.: 15.0～100mm W.T.: 2～10mm
Hot rolled: O.D.: 25~700mm W.T.: 3~50mm
Grade: Gr.A ,Gr.B, Gr.C.
Length: 6M or specified length as required.
Ends: Plain End, Beveled End, Threaded
Mechanical and NDT Tests for ASTM A106 Black Seamless Steel Pipe
Bending Test— a sufficient length of pipe shall stand being bent cold through 90° around a cylindrical mandrel.
Flattening test-although testing is not required, pipe shall be capable of meeting the flattening test requirements.
Hydro-static test—except as allowed, each length of pipe shall be subjected to the hydro-static test without leakage through the pipe wall.
Nondestructive electric test-as an alternative to the hydro-static test, the full body of each pipe shall be tested with a nondestructive electric test. 

评论

发表评论

此博客中的热门博文

ASTM A213 T11 Alloy Seamless Steel Boiler Tubes

图片
ASTM A213 T11 Alloy Seamless Steel Boiler Tubes Standard: ASTM A213/ASME SA213 Application of ASTM A213 Alloy Seamless Steel pipe s : Pipe ordered under this specification is for manufacturing wall panel, economizer, superheater and steam pipeline of boilers Manufacturing Process of ASTM A213 Alloy Seamless Steel Tubes : ASTM A213 alloy seamless steel tubes are produced either by cold-drawn or hot rolled, as specified. Grade TP347HFG shall be cold finished. Heat treatment shall be done separately and in addition to heating for hot forming. The ferritic alloy and ferritic stainless steels shall be reheated. On the other hand, austenitic stainless steel tubes shall be furnished in the heat-treated condition. Alternatively, immediately after hot forming, while the temperature of the tubes is not less than the minimum solution temperature, tubes may be individually quenched in water or rapidly cooled by other means. Details of ASTM Boiler Tube   We can supply: Manufact...
阅读全文

BS EN10210 S275J0H LSAW(JCOE) Steel Pipe

图片
BS EN10210 S275J0H LSAW(JCOE) Steel Pipe This specification covers carbon steel pipe  for high-temperature service. Application of EN10210 S275J0H LSAW Steel Pipe: Pipe ordered under this specification is used for structural. Manufacturing Process: Electric fusion welded LSAW steel pipe Details of EN10210 LSAW JCOE STEEL PIPE  We can supply: Manufacture: Seamless Steel Pipe Size: O.D.: 323.8~1500mm W.T.: 6~80mm Grade: S355J0H, S355J2H, S355J2H, S275J0H, etc. Length: 6M or specified length as required. Ends: Plain End, Beveled End Mechanical Properties  of Non Alloy Steel Pipe MECHANICAL PROPERTIES Steel Grade Minimum Yield Strength (Mp) Tensile Strength (Mp) Specified Thickness (mm) Specified Thickness (mm) Steel Name Steel Number ≤16 ＞16≤40 ＞40≤63 ＞63≤80 ＞80≤100 ＞100≤120 ≤3 ＞3≤100 ＞100≤120 S275J0H 1.0149 275 265 255 245 235 225 430-580 410-560 400-540
阅读全文

What are the Causes and Countermeasures for Lateral Cracking of Stainless Steel Products?

图片
As an  Alloy Seamless Steel Tubing Supplier , share with you. Stainless steel products often have various cracking phenomena during the drawing process. Among them, lateral or point cracking of the side walls is a common form of processing failure of 304 stainless steel products with relatively deep drawing such as vacuum cups and pressure cookers. Especially in recent years, the product processing process has been continuously promoted. For example, the number of drawing passes of the thermal insulation cup has been reduced from 5 times to 3 times commonly used at present, from multiple annealing in the middle to one annealing or no annealing after the completion of stamping. Therefore, higher requirements are imposed on the formability of stainless steel materials. The occurrence of lateral or point-like cracking defects on the side walls of stainless steel products may be caused by intercrystalline defects of materials, delta ferrite and other materials, or it may be caused by ...
阅读全文